煜瑞物资滚筒包胶流程 一：打磨滚筒 将滚筒上的残胶清理掉，然后使用专用的打磨机在滚筒上打磨出粗糙无 锈蚀点的表面，最后使用纤维碟轻轻打磨一遍. Remove the old rubber on the pulley, then use special grinder to buff the surface until it*s smooth and no rust exist, finally buff the surface gentally with the fibre disc. 二：漘洗表面 用清扫刷将打磨面清扫干净，然后再用TIP TOP清洗剂进行清洗.确保滚 筒表面无任何残留物。若滚筒表面有水，则应待其干燥。 Clean the buffing dust of the surface, then wash it with special cleani -ng solvent. Make sure no residue remains.lf part of the pulley is wet, dry it first. 三：涂粘接剂 先将PR200金属处理剂薄而均匀的涂刷在滚筒打磨面上.待其完全千 透。然后将按特定比例配合的SC2000/UTR固化剂搅拌均匀，在筒体上 用力而均匀的涂刷一遍，待其彻底干燥，再涂刷第二次，同时在胶板的 背面也涂刷一遍4 Apply one thin and even coat of PR200 solvent on the buffing surface, wait until it's completely dry . Then mix the SC2000 and UTR hardener according to certain ratio,stir it adquately, then coat the pulley surface with the mixture, apply a second coat when the first is dried thorough -ly, Whie the second coat proceed, apply one coat on the back of the rubber board. 四：粘貼胶板 待SC2000干至略有粘性但不附着在指背时进行粘貼胶板.并用压实滚轮 滚压，用橡胶锤将胶板锤打结实，确保内部无气泡，最后使用T2胶枪填 充接缝. 并对边缘进行打磨修整^ Test the second coat with finger back, when it*s a bit tacky, apply the rubber board on the pulley surface exactly, and press it with stitcher, then hammer it with rubber mallet. Make sure no bubble is trapped. Finally fill the gap with T2 GUN, and trim the edge. TIPS: *传统热硫化包胶，需使用大型热压硫化设备，操作复杂，消耗时间长。 *由于需搬运至硫化工作间操作， 故对滚筒进行热硫化包胶需同等数量的备用滚筒， 造成资源极度浪费。 *使用热硫化方式包胶前， 必须先在金属滚筒表面雕刻出至少3毫米的沟槽， 才能确保橡胶与滚筒粘接良好， 该种操作方式将会对滚筒的使用寿命产生致命影响(同等条件下， TIP TOP冷硫化包胶仅需将滚筒表面打磨光滑即可)。 *传统热硫化包胶橡胶硫含量较高，硫化时压力不够，橡胶易老化，不耐磨。 煜瑞物资滚筒包胶采用久负盛名的SC2000为粘接剂， 使得滚筒与表层橡胶之间借助CN粘接层在常温下进行冷硫化结合,硫化压强为热硫化数倍，硫化速度极快，且粘接强度极为强劲。煜瑞物资德国原产的特种橡胶耐磨性极好，弹性佳，且可防止物料粘附，具有超长的使用寿命。